| PROPERTY | TEST METHOD (ASTM D) | CONDITION | VALUE | UNIT |
|---|---|---|---|---|
| Special Gravity | ASTM D 792 | 0.6 | g/cm3 | |
| Water Absorption | ASTM D 570 | 76.2mm x 25.4mm; Drying: 50°C, 24 hrs; Immersion: 25°C, 24 hrs | 0.37 | % |
| Shore D Hardness | ASTM D 2240 | Type D | 70 | D |
| Mechanical Fastener holding Capacity | ASTM D 1037 | 170 | kg | |
| Screw Holding Capacity | With 1/6 wood screw plate to plate | 40 | kg | |
| Screw Bonding Capacity | With 1/6 wood screw plate to plate | 24 | kg | |
| Tensile Strength at Yield | Specimen: Type 1, Speed: 10 mm/min | 10 MPa | 1450 psi | |
| Elongation Break | ASTM D 638 | Specimen: Type 1, Speed: 10 mm/min | 8 | % |
| Tensile Modulus | Specimen: Type V,Speed: 1 mm/min | 700 | MPa | |
| Flexural Strength | ASTM D 790 | 127 mm x 12.91 mm x 3.77 mm | 20 MPa | 2900 psi |
| Flexural Modulus | Speed: 1.6 mm/min Span: 59 mm | 1210 MPa | 175450psi | |
| Impact Strength | ASTM D 6110-06 | Width: 6.65 mm; Depth: 12.86 mm; Heating Rate: 120°C/h; Load 0.455 MPa | 25 | J/m |
| Dielectric Strength | ASTM D 149 | 10 | kv/mm | |
| Heat Deflection | ASTM D 648-07 | Width: 6.65 mm; Depth: 13.07 mm; Heating rate: 120°C/h; Local: 1.82 MPa | 61.4 | °C |
| Temperature | Method B | Width: 6.65 mm; Depth: 12.85mm; Heating rate: 120°C/h; Local: 0.455 MPa | 70.9 | °C |
| Heat Distortion Temp. (Under load at 246 psi) | ASTM D 648 | 120 | °C | |
| Co-efficient of Linear Expansion | ASTM D 696 | 2.9x10-5 | in/in/°F | |
| Thermal Conductivity | ASTM D 177 | 0.06 | W/m°K | |
| Flamability | GB/T 8624-2006 81 | Passed | ||
| Horizontal Burning | ASTM F635-06 | Specimen: 127mm x 12.6mm x 12.74mm | Burning rate: 0 mm/min |